WC-Co Powder with strong Wear-Resistance
Short Description:
Description
WC-Co Powders: High-Performance Materials for Wear-Resistant Applications
Introducing our range of WC-Co powders, designed to provide exceptional wear resistance and durability in a wide range of industrial applications. Our powders are made of tungsten carbide (WC) particles held together by cobalt (Co) binder, resulting in a material that is both hard and tough.
Our product range includes four main grades: KF-60 WC-12Co, KF-61 WC-17Co, and KF-62 WC-25Co, each with varying cobalt content and particle size distribution. KF-60 is available in both sintered and crushed or agglomerated and sintered forms, with particle sizes ranging from 15-45μm and 10-63μm, respectively. KF-61 and KF-62 are both agglomerated and sintered powders, with particle sizes ranging from 15-45μm and 10-38μm.
Our WC-Co powders offer excellent wear resistance and are particularly suited for applications where there is a high level of friction, such as in general machinery or fretting wear environments. The higher cobalt content in KF-61 and KF-62 provides better toughness, making them ideal for applications where impact resistance is also required.
In addition to their exceptional wear resistance, our WC-Co powders are also highly versatile and can be used in a variety of ways. They can be sprayed onto surfaces to form a hard and wear-resistant coating, or they can be used to manufacture wear-resistant components such as cutting tools, bearings, and seals.
At our state-of-the-art production facility, we use advanced processing techniques to ensure consistent and high-quality powders. Our products are rigorously tested to ensure they meet the highest standards for wear resistance and durability.
In summary, our range of WC-Co powders is a reliable choice for industrial applications where wear resistance and durability are critical. With their exceptional properties and versatility, they provide a cost-effective solution for extending the life of components and improving the performance of machinery.
Similar Products
| Brand | Product Name | AMPERIT | METCO/AMDRY | WOKA | PRAXAIR | PAC |
| KF-60P | WC-12Co | 515 | 72F-NS | WC-114WC-489-1 | 127 | |
| WC-12Co | 518519 | 3101-3106 | WC-7271342 | 125126 127 |
||
| KF-60C | WC-12Co(Low Carbon) | 512 | ||||
| KF-61P | WC-17Co | 526 | 5143 2005NS 73F-NS | 32023202 | WC-7291343 | |
| KF-62 | WC-25Co |
Specification
| Brand | Product Name | Particle Size (μm) | Chemistry (wt%) | Type | Apparent density | Flowability | Properties | Application | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Co | C | Fe | W | Cr | B | Si | Ni | ||||||||
| KF-65 | WC-10Co4Cr | 15-45, 10-38 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Sinter&Crush | 5.5-6.5g/cm3 | ≤25 s/50g | APS，HVOF,HVAF | Alternative hard chromium plating; Petroleum, paper, general machinery | |||
| KF-65 | WC-10Co4Cr | 15-45,10-38,5-30 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS，HVOF,HVAF | Alternative hard chromium plating; Petroleum, paper, general machinery | |||
| KF-65 | WC-10Co4Cr | 5-25，5-15 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated and sintered | 3.5-4.8 g/cm3 | Stable feeding to powder feeder | HVOF,HVAF | Alternative hard chromium plating；Smoother surface, less or free post machining； | |||
| KF-60 | WC-12Co | 15-45，10-63 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Sinter&Crush | 5.5-6.5 g/cm3 | ≤25 s/50g | APS，HVOF | Wear resistance，Fretting wear resistance | ||||
| KF-60 | WC-12Co | 15-45，10-38，5-30 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS，HVOF，HVAF | Wear resistance，Fretting wear resistance；general machinery | ||||
| KF-61 | WC-17Co | 15-45，10-38 | 15.5-17 | 4.5-5.1 | ≤0.8 | Bal. | Agglomerated and sintered | 3.5-5.5 g/cm3 | ≤25 s/50g | APS，HVOF，HVAF | Wear resistance，Fretting wear resistance，Better toughness； general machinery | ||||
| KF-62 | WC-25Co | 15-45，10-38 | 22-26 | 4.0-4.6 | ≤0.8 | Bal. | Agglomerated and sintered, Densification | 3.0-5.5 g/cm3 | ≤25 s/50g | APS, Detonation guns，cold spray | Fretting wear resistance，Better toughness | ||||
| KF-66 | WC-23%CrC-7Ni | 15-45，10-38 | 6.0-6.8 | ≤0.8 | Bal. | 16.5-20 | 5.5-7 | Agglomerated and sintered | 3.0-5.0 g/cm3 | ≤25 s/50g | APS，HVOF,HVAF | Alternative hard chromium plating；Used for low concentration acid/alkali environment at 200 ℃; Anti oxidation and wear resistance at 750 ℃ | |||
| KF-66 | 43WC-43%CrC-14Ni | 15-45,10-38 | 7.8-8.4 | ≤0.8 | Bal. | 35-38 | 12-14 | Agglomerated and sintered | 2.0-4.0 g/cm3 | ≤35 s/50g | APS，HVOF，HVAF | Alternative hard chromium plating Used for low concentration acid/alkali environment at 200 ℃ | |||
| KF-63 | WC-10Ni | 15-45,10-38 | 4.5-5.2 | ≤0.1 | Bal. | 8.5-10.5 | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS，HVF，HVAF | Non magnetic wear resistant coating. Better corrosion resistance | ||||
| KF-70 | Cr3C2-25NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 18-21.5 | Agglomerated and sintered | ≥2.3 g/cm3 | Stable feeding to powder feeder | APS，HVOF | Anti oxidation and wear resistance at 815 ℃ | ||||
| KF-69 | Cr3C2-20NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated and sintered | ≥2.3 g/cm3 | Stable feeding to powder feeder | APS，HVOF | Anti oxidation and wear resistance at 815 ℃ | ||||
| KF-71 | Cr3C2-30NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated and sintered | ≥2.3 g/cm3 | Stable feeding to powder feeder | APS，HVOF | Anti oxidation and wear resistance at 815 ℃. Better toughness | ||||
| KF-60 | WC-12Co (Low Carbon) | 15-45, 20-53 | 10.5-12 | 4.0-4.4 | ≤0.8 | Bal. | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | HVOF,HVAF | Used for Zn bath rolls in Continuous Galvanizing Lines | ||||
| KF-68 | WC-30WB-10Co | 15-45,20-53,10-38 | 9-11 | 3.5-3.9 | Bal. | 1.4-1.7 | Agglomerated and sintered | 3.0-4.9 g/cm3 | ≤30 s/50g | HVOF,HVAF | Used for Zn bath rolls in Continuous Galvanizing Lines | ||||
| KF-68 | WC-30WB-5Co5Cr | 15-45,20-53,10-38 | 4-6 | 3.5-3.9 | Bal. | 4-6 | 1.4-1.7 | Agglomerated and sintered | 3.0-4.9 g/cm3 | ≤30 s/50g | HVOF,HVAF | Used for Zn bath rolls in Continuous Galvanizing Lines | |||
| KF-300E | 35%WC-NiCrBSi | 15-53,45-104 | 2.5-3.2 | 1.0-2.6 | 32-35 | 7.5-9 | 1.5-1.9 | 2.0-2.7 | Bal. | WC and NiCrBSi forming alloy | 4.0-4.9 g/cm3 | ≤16 s/50g | HVOF，PS | Alternative Blended type WC+Ni60；Higher material utilization，Lower energy consumption, lower thermal impact；Used for glass mold | |
| KF-300F | 50%WC-NiCrBSi | 15-53,45-104 | 3.2-4.3 | 0.8-2.0 | 45-48 | 5.8-7.2 | 1.0-1.7 | 1.5-2.4 | Bal. | WC and NiCrBSi forming alloy | 5.0-7 g/cm3 | ≤16 s/50g | HVOF，PS | ||